请帮忙译成英文，谢谢！急急急急！

We shop to mould this morning to discuss the mould about HT this paragraph of modification plan; The following is the solution for your reference, thank you!

1: if do 55 'c, which in the second mold of the hot and cold cuts, hardness will achieve the 60' c; That is, the more hard which EVA do footbed hardness would be more hard will not become soft;

2: if footbed hardness to do 40, that there is no way to do, the reason is EVA which is too soft EVA will crack;

3: if footbed hardness to do 40, that shoes also can appear in molding, because stockfitting shoes need on the assembly line, the pipeline temperature is probably about 50 'C, high temperature footbed EVA will swell and can't withdraw; It will cause deformation;

4: outsole shop will today which MOULD thickening;

5: the MOULD SHOP today will take to modify footbed mold Eva, Foobed Eva positive plane in position, plus a couple pinhole;

6: we expect outsole shop will try again tomorrow to show us a few double samples; I'll tell you the news;

7: after all the technical personnel's research, hope the hardness retained in 48 EVA, 'c hope can be you adopt;